Eka Nurfani, Aldi Saputra, Novalia Pertiwi, Muhamad F. Arif
In this paper, Ni-doped ZnO films were grown on a p-type silicon substrate via spray pyrolysis. The Ni dopant concentrations were varied by adjusting the weight ratio between Zinc Acetate Dehydrate (ZAD) and Nickel Chloride Hexahydrate (NCH), resulting in the ZnO, ZnO:Ni1%, and ZnO:Ni3% samples. Field-effect scanning electron microscopy (FESEM) images revealed that Ni doping significantly reduced the nanostructure size from 326 nm (ZnO) to 146 nm (ZnO:Ni3%). Similarly, X-ray diffraction (XRD) analysis also shows the decrease of the crystallite size with increasing Ni doping, from 44 nm (ZnO) to 35 nm (ZnO:Ni3%). Current–voltage (I–V) measurements were conducted at a bias voltage of 0 and 5 V to examine electrical and self-powered photodetection properties. All samples demonstrate self-powered photodetector performance. At the bias of 0 V, the undoped ZnO exhibited a higher photo-to-dark-current ratio (162) as compared to ZnO:Ni1% (18) and ZnO:Ni3% (16). The ZnO:Ni3% samples displayed faster rise (0.4 s) and fall times (1.7 s) as compared to the pure ZnO (10.8 s for rise time and 9.1 s for fall time), highlighting their potential for applications requiring rapid photoresponse. The findings provide valuable insights into optimizing the performance of ZnO-based photodetectors through controlled Ni doping, enabling advancements in self-powered photodetection technology for energy-efficient optoelectronic devices. © 2025
Department of Materials Engineering, Faculty of Industrial Technology, Institut Teknologi Sumatera (ITERA), South Lampung, 35365, Indonesia; Center for Green and Sustainable Materials, Institut Teknologi Sumatera (ITERA), South Lampung, 35365, Indonesia; Department of Telecommunication Engineering, Faculty of Industrial Technology, Institut Teknologi Sumatera (ITERA), South Lampung, 35365, Indonesia
Research at a Glance
Register to unlock
Topics & SDG Alignment
Register to unlock
Collaboration
Register to unlock
Author Profile (Selected)
Register to unlock
References Overview
Register to unlock
Journal & Source
Register to unlock
Metadata & Integrity
Register to unlock