Wiwien Andriyanti, Maureen Annisatul Choir Hidayati Nur, Deska Lismawenning Puspitarum, Tjipto Sujitno, Hari Suprihatin, Setyo Purwanto, Edi Suharyadi
This study investigates the properties and performance of bismuth ferrite thin films on Kapton sheets as electromagnetic (EM) wave-absorbing materials. The main techniques employed in this study involved modifying the surface geometry and using electromagnetic wave-absorbing materials as surface coatings. X-ray diffraction analysis revealed a cubic crystal structure of the bismuth ferrite thin films. The bonding analysis showed the presence of Bi–O and Fe–O functional groups at 432.26 and 519.48 cm−1, respectively. Vibrating-sample magnetometry revealed the ferromagnetic behavior of the bismuth ferrite thin film, confirming that saturation magnetization decreased with increasing sputtering time. Moreover, the calcination temperature affected the coercive field; the higher the calcination temperature, the higher the coercivity of the BiFeO3 (BFO) thin film layer. Scanning electron microscopy with energy-dispersive X-ray spectroscopy of the bismuth ferrite thin films revealed the presence of Bi, Fe, and O—evenly and homogeneously distributed on the Kapton surface. After the ion implantation process, the atomic force microscopy test results showed an increased root-mean-square roughness (Rq). The root-mean-square roughness value for Kapton before the process was approximately 7.5 nm, while the root-mean-square roughness values for BFO 10 min and BFO 12.5 min were approximately 18.8 nm and 25.3 nm, respectively. The microwave absorption ability reached a maximum reflection loss value of − 40.4 dB (99.9 %) in the range of 9.98 GHz with a sputtering duration of 10 min. Therefore, these results suggest bismuth ferrite is a potential candidate as an EM wave absorber. © 2024 Elsevier B.V.
Department of Physics, Universitas Gadjah Mada, Yogyakarta, Indonesia; Research Center for Advanced Material, National Research and Innovation Agency, Indonesia; Department of Physics, Institut Teknologi Sumatera, Lampung, Indonesia; Research Center for Accelerator Technology, National Research and Innovation Agency, Indonesia; Directorate of Laboratory Management, Research Facilities, and Science and Technology Park, National Research and Innovation Agency, Indonesia
Research at a Glance
Register to unlock
Topics & SDG Alignment
Register to unlock
Collaboration
Register to unlock
Author Profile (Selected)
Register to unlock
References Overview
Register to unlock
Journal & Source
Register to unlock
Metadata & Integrity
Register to unlock