In an enzyme-based fuel cell system, glucose oxidase and laccase were immobilized on carbon paper as the anode and cathode electrodes. A conductive polymer (polypyrrole) was added to improve conductivity. The mediator and enzymes were mixed in a phosphate-buffer solution for entrapment. A Nafion 212 membrane separated the two half-cells. Power density measurements were taken at a glucose concentration of 10 mM across different operating voltages. Potassium hexacyanoferrate III was used as a redox mediator in the anode and 2,2′-azino-bis (3-ethylbenzothiazoline-6-sulfonic acid) in the cathode to boost power output. The biofuel cells, constructed from acrylic (40 × 50 × 50 mm) with a working volume of 20 × 30 × 40 mm, were assembled using a rubber gasket to secure the Nafion membrane. The use of micropore tape covering the electrodes extended the system’s operational lifespan. Without the micropore tape, the maximum power density was 57.6 μW/cm2 at 0.24 V. With the micropore tape, the cell achieved a maximum power density of 324.9 μW/cm2 at 0.57 V, sustaining performance for 20 days. Thus, micropore tape effectively enhances enzyme retention and biofuel cell performance. © 2025 by the authors.
Department of Chemical Engineering and Materials Science, Yuan Ze University, 135 Yuan Tung Road, Chung Li, Taoyuan, 32003, Taiwan; Department of Chemical Engineering, Institut Teknologi Sumatera, Bandur Lampung, 35365, Indonesia